The influences of W doping at Mn site on the charge order and spin order were studied by measuring M-T curves, M-H curves and ESR spectra of La0.3Ca0.7Mn1?xWxO3 (x = 0.00, 0.04, 0.08, 0.12, 0.15) system. The results showed that: When 0.00≤ x≤0.08, the system exhibits charge ordering (CO) phase, and its spin order experiences the change of paramagnetism (PM)-charge ordering (CO)-antiferro- magnetism (AFM) with decreasing temperature; when x≥0.12, the charge ordering (CO) phase melts, part of charge ordering (CO)phase remains in the paramagnetism (PM)background, the spin order of the system is mainly paramagnetism (PM), and ferromagnetic (FM) clusters appear at low tem- perature.
LIU NingYAN GuoqingCAI ZhirangGUO HuanyinPENG ZhenshengQU ZheZHANG Yuheng
用固相反应法制备了Y1-xDyxCrO3(x=0,0.1)多晶样品。通过X射线衍射(XRD)图谱检测了样品的结构,测量了样品的磁性,作了磁化强度-温度(M-T)曲线、磁化强度-磁场(M-H)曲线,研究了Dy3+替代Y3+对Y1-xDyxCrO3体系磁性质的影响。结果表明,Dy3+替代多铁性YCrO3中的Y3+对YCrO3的磁性有效大影响。YCrO3在奈尔温度TN=139 K以下呈倾角反铁磁,显示弱铁磁性;Dy3+替代Y3+后的Y0.9Dy0.1CrO3样品,在50 K
通过测量样品的磁化强度-温度曲线、电阻率-温度曲线及磁电阻-温度曲线.研究了 Dy 掺杂(0.00≤x≤0.30)对 La_(0.7-x)Dy_xSr_(0.3)MnO_3 体系磁电性质的影响.实验发现,随 Dy 掺杂量的增加,体系磁结构从长程铁磁有序向自旋团簇玻璃态、反铁磁状态转变；x=0.20、0.30时的低温磁行为发生异常,电行为存在低温电阻率极小值现象.这些奇特现象不仅来源于掺杂引起的晶格效应,也来源于掺杂引起的额外磁性耦合.