V2O5 films were prepared on silicon wafers by DC magnetron sputtering and post-annealing under various conditions. The influence of depositing and post-annealing temperatures on microstructure of V2O5 films was studied by XRD and Raman scattering measurements. The results reveal that sputtered V2O5 films show preferred growth orientation along (001) planes and the c-axis is perpendicular to the silicon substrate surface. It is interesting to find that both the V2O5 film deposited at temperature of 511 ℃ and the one annealed at 500 ℃ exhibit desirable layer-type structure of orthorhombic symmetry. Such layer-typed V2O5 films are promising candidates for cathodes of rechargeable lithium or magnesium thin-film batteries.
SU Qing PAN Xiaojun XIE Erqing WANG Yinyue QIU Jiawen LIU Xueqin
Vanadium oxide nanotubes were synthesized by hydrothermal treatment from V2O5·nH2O sols as precursor and dodecylamine as structure-directing template. The morphology and structure of the nanotubes were characterized by SEM, TEM, XRD, TG-DTA and FTIR. The experimental results reveal that the duration of the hydrothermal treatment is of importance for obtaining VOx-NTs which have a layered structure. TG-DTA study indicates that V5+ cations in nanotubes are partially reduced to V4+ cations. The results from FTIR spectra indicate the difference in V-O vibrations between before and after hydrothermal treatment. From the results, it suggests that during hydrothermal treatment, the rearrangement of the vanadium oxide structure leads to the formation of VOx nanotubes from lamellar structure because of the presence of V4+ species.
HUANG Chunming LIU Xueqin KONG Lingbin ZHOU Haijia LIU Yaqiang QIU Jiawen WANG Yinyue