Nanosized TiO2 particles were prepared by solvothermal method using tetrabutyl titanate as precursor,ethanol and water as solvents,and a facile immobilization method of nanosized TiO2 particles on woven glass fabric was developed. The samples obtained under various preparation conditions were charac-terized by means of thermo gravimetric analysis(TG) and differential scanning calorimetry(DSC) ,X-ray diffraction(XRD) ,transmission electron microscopy(TEM) ,high resolution-transmission electron mi-croscopy(HR-TEM) ,and Brunauer-Emmett-Teller(BET) . The results show that the cube-shape of TiO2 prepared by solvothermal method has good crystallinity of(101) surface,higher thermal stability and large specific surface area. Scanning electron microscopy(SEM) images confirmed that the immobi-lized TiO2 film was uniformly distributed and clung to the substrate firmly. The photocatalytic activity of the catalysts was tested using photocatalytic oxidation of gaseous benzene. The results show that the TiO2 calcined after solvothermal treatment suffers from lower specific surface area,and hence de-creases its photocatalytic activity. The photocatalytic activities of the TiO2 by solvothermal treatment with or without calcination in degradation 400 mg/m3 benzene are 3.7 and 4.1 times as high as catalyst without solvothermal treatment,respectively.
WU ZhongBiao GU ZhuoLiang ZHAO WeiRongt WANG HaiQiang