A series of oxygen permeable dual-phase composite oxides 60 wt% Ce0.8Gd0.2O2-δ-40 wt% Ln Ba Co2O5+δ(CGO-LBCO, Ln = La, Pr, Nd,Sm, Gd and Y) were synthesized through a sol-gel route and effects of the Ln3+cations on their phase structure, oxygen permeability and chemical stability against CO2 were investigated systemically by XRD, SEM, TG-DSC and oxygen permeation experiments. XRD patterns reveal that the larger Ln3+cations(La3+, Pr3+and Nd3+) successfully stabilized the double-layered perovskite structure of sintered LBCO,while the smaller ones(Sm3+, Gd3+, and Y3+) resulted in the partial decomposition of LBCO with some impurities formed. CGO-PBCO yields the highest oxygen permeation flux, reaching 2.8×10-7mol s-1 cm-2at 925?C with 1 mm thickness under air/He gradient. The TG-DSC profiles in 20 mol% CO2/N2 and oxygen permeability experiments with CO2 as sweep gas show that CGO-YBCO demonstrates the best chemical stability against CO2, possibly due to its minimum basicity. The stable oxygen permeation flux of CGO-YBCO under CO2 atmosphere reveals its potential application in the oxy-fuel combustion route for CO2 capture.
Ba0.9R0.1Co0.7Fe0.225Ta0.075O3-δ(BRCFT, R = Ca, La or Sr) membranes were synthesized by a solid-state reaction. Metal cation Ca2+,La3+or Sr2+doping on A-site partially substituted Ba2+in BaCo0.7Fe0.225Ta0.075O3-δoxides, and its subsequent effects on phase structure stability, oxygen permeability and oxygen desorption were systematically investigated by XRD, TG-DSC, H2-TPR, O2-TPD techniques and oxygen permeation experiments. The partial substitution with Ca2+, La3+or Sr2+, whose ionic radii are smaller than that of Ba2+, succeeded in stabilizing the cubic perovskite structure without formation of impurity phases, as revealed by XRD analysis. Oxygen-involving experiments showed that BRCFT with A-site fully occupied by Ba2+exhibited good oxygen permeation flux under He flow, reaching about 2.3mL min-1 cm-2at 900 ℃ with 1 mm thickness. Of all the membranes, BLCFT membrane showed better chemical stability in CO2, owing to the reduction in alkalinity of the mixed conductor oxide by La doping. In addition, we also found the stability of the perovskite structure under reducing atmospheres was strengthened by increasing the size of A-site cation(Ba2+>La3+>Sr2+>Ca2+).
Bo JiangHongwei ChengLongfei LuoXionggang LuNaijun ZhangJizhong Liu