Aromatization of methanol over co-impregnated La/Zn/HZSM-5 zeolite catalyst was studied.The selectivity of aromatics and BTX(benzene,toluene,and xylene)reached 64.0%and 56.6%,respectively,using La/Zn/HZSM-5 at 437°C,0.1 MPa and methanol WHSV(weight hourly space velocity)=0.8 h-1.Catalytic results showed that the La species was a very good promoter,increased selectivity of aromatics,and prolonged the catalyst lifetime on stream.The effects of the SiO2/Al2O3 ratio in zeolite,Zn and La loading,WHSV,reaction temperature, water content in the feed and H2 pretreatment of catalysts on the catalytic performance were studied in detail. Characterizations of the catalysts by thermogravimetric analysis(TGA),NH3-TPD(temperature programmed desorption),SEM(scanning electron micrograph),N2 adsorption-desorption,XRD(X-ray diffraction)and XRF (X-ray fluorescence),were carried out to understand the structure and discuss the aromatization performance of La/Zn/HZSM-5 zeolite catalyst.
The hierarchical mesoporous Zn/ZSM-5 zeolite catalyst was prepared by NaOH treatment and Zn impregnation, and its application in the conversion of methanol to gasoline (MTG) was studied. N2 adsorption-desorption results showed that the mesopores with sizes of 2–20 nm in HZ5/0.3AT was formed by 0.3 M NaOH alkali treatment. The zeolite samples after modification were also characterized by XRF, AAS, XRD, SEM and NH3-TPD methods. Zn impregnated catalyst Zn/HZ5/0.3AT exhibited dramatic improvements in catalytic lifetime and liquid hydrocarbons yield. The selectivity of aromatic hydrocarbons was also improved after Zn impregnation. It is suggested that the mesopores of Zn/HZ5/0.3AT enhanced the synergetic effect of Zn species and acid sites and the capability to coke tolerance, which were confirmed by the results of catalytic test and TGA analysis, respectively.
Youming NiAiming SunXiaolingWuGuoliang HaiJianglin HuTao LiGuangxing Li