In the present work transparent Y2O3 ceramics were made by slip casting and vacuum sintering of nanopowders with sodium poly-acrylic acid(PAA-Na) as dispersant.The rheological properties of Y2O3 nanopowder slurry were investigated using different amounts of dis-persant and solid contents.The microstructures and transmittance of the sintered ceramics were also studied by means of scanning electron microscopy(SEM) and ultra-violet visible spectrometry.The results showed that rheological behaviors of the Y2O3 nanopowder slurry were effectively promoted by sodium polyacrylic acid.Highly dispersive and stable slurries were obtained as the dispersant was added over 1.0 dwb% under the fixed conditions of pH 11 and 45 wt.% solid content.All the slip cast green bodies were sintered into highly dense ceramics after sintering at 1700 oC for 5 h in vacuum,wherein the sample added with 1.1% sodium polyacrylic acid exhibited the highest relative den-sity of 99.36% and transmission of 30% at 800 nm wavelength.
研究了Al2O3/Ti(C,N)-Ni-Ti陶瓷复合刀具对淬硬35CrMo合金钢进行连续干切削时各切削参数对切削力的影响.结果表明:切削深度对切削力的影响最显著,切削速度的影响最小.对比研究了Al2O3/Ti(C,N)和Al2O3/Ti(C,N)-Ni-Ti陶瓷刀具的耐磨性能和磨损形态:后者的耐磨性能明显优于前者,其中Al2O3/Ti(C,N)-5%(Ni,Ti)的耐磨性能最高.Al2O3/Ti(C,N)-Ni-Ti刀具的磨损形态主要表现为后刀面的磨粒磨损和疲劳磨损,由于这种材料具有较高的弯曲强度和断裂韧性,能有效防止前刀面出现崩刃破损现象,因此具有较高的可靠性,适用于高速切削.在高速切削条件(ap=0.06 mm,vc=254.9 m/min,vf=0.09 mm/r)下,Al2O3/Ti(C,N)-5%(Ni,Ti)刀具的切削耐用度为150 min.