Microstructures and mechanical properties of the 25Mn twinning induced plasticity (TWIP) steel at different annealing temperatures were investigated. The results indicated that when the annealing temperature was 1000°C,the 25Mn steel showed ex-cellent comprehensive mechanical properties,the tensile strength was about 640 MPa,the yield strength was higher than 255 MPa,and the elongation was above 82%. The microstructure was analyzed by optical microscopy (OM),X-ray diffraction (XRD),and transmission electron microscopy (TEM). Before deformation the microstructure was composed of austenitic matrix and annealing twins at room temperature; at the same time,a significant amount of annealing twins and stacking faults were observed by TEM. Mechanical twins played a dominant role in deformation and as a result the mechanical properties were found to be excellent.
Zhen-li Mi Di Tang Hai-tao Jiang Yong-juan Dai Shen-sheng Li
The influence of cold rolling reduction on microstructure and mechanical properties of the TWIP (ttwinning induced plasticity) steel was investigated. The results indicated that the steel had better comprehensive mechanical properties when cold rolling reduction was about 65.0% and the annealing temperature was 1000℃. The tensile strength of the steel is about 640MPa and the yield strength is higher than 255MPa, while the elongation is above 82%. The microstructure is composed of austenitic matrix and annealing twins at room temperature, at the same time, a significant amount of annealing twins and stacking faults are observed by transmission electron microscopy (TEM). Mechanical twins play a dominant role during deformation, and result in excellent mechanical properties.