Numerical simulation of hot-press sintering of nano-sized ceramic powders was introduced by the commercial finite element code MSC.MARC. The powder plastic model and the thermo-mechanical coupled quadrilateral element were developed and adopted in the simulation. The mechanical and thermal properties of the nano-sized alumina based powders were determined.In addition, the experimental research and numerical simulation of the sintering process of different initial densities were carried out. The stress state in sintering of green compacts with different initial densities was analyzed by the densification theory.The reason for the density fluctuations of as-sintered ceramic bulks was found out.
Guoqing CHEN Kaifeng ZHANG Guofeng WANG Yandong YU
A series of alumina-zirconia composites with various grain sizes were prepared from the nano-sized powders with different agglomerations. Microstructural analysis of the sintered compacts indicates that the as-sintered material is a typical intra/inter granular nanocomposite with uniform distribution of the zirconia grains in the alumina matrix.Superplastic deep drawing test under different conditions demonstrates that dense Al2O3/ZrO2 samples with average grain size of 230 nm can be elongated to a dome height of at least 12 mm at the punch rate of 0.6 mm.min-1at 1400℃. Further drawing tests show that for the composites with larger grain size, such elongation cannot be achieved at such a strain rate.
Guoqing CHEN, Kaifeng ZHANG, Wenbo HAN and Junting LUOSchool of Materials Science and Engineering, Harbin Institute of Technology, Harbin 150001, ChinaProf., Ph.D.,