Boron- and cerium-codoped TiO2 photocatalysts were synthesized using modified sol-gel reaction process and characterized by X- ray diffraction （XRD）, X-ray photoelectron spectroscopy （XPS）, particle size distribution （PSD）, diffuse reflectance spectra （DRS）, and Brunauer-Emmett-Teller （BET）. The photocatalytic activities were evaluated by monitoring the degradation of dye Acid Red B （ARB）. The results showed that the prepared photocatalysts were mixed oxides mainly consisting of titania, ceria, and boron oxide. The structure of TiO2 could be transformed from amorphous to anatase and then to rutile by increasing calcination temperature; the transformation being accompanied by the growth of particle size without any obvious change in phase structure of CeO2. The XPS of B1.6Ce1.0-TiO2 prepared at 500℃ showed that a few boron atoms were incorporated into titania and ceria lattice, whereas others existed as B2O3. Cerium ions existed in two states, Ce^3＋ and Ce^4＋, and the atomic ratio of Ce^3＋/Ce^4＋ was 1.86. When boron and cerium were doped, the UV-Vis adsorption band wavelength showed an obvious shift toward the visible range （〈526 nm）. As the atomic ratio of Ce/Ti increased to 1.0, the absorbance edge wavelength increased to 481 nm. The absorbance edge wavelength decreased for higher cerium doping levels （Ce/Ti=2.0）. The particles size ranged from 122 to 255 nm with a domain at 168 nm （39.4%）. The degradation of ARB dye indicated that the photocatalytic activities of boron- and cerium-codoped TiO2 were much higher than those of P25 （a standard TiO2 powder）. The activities increased as the boron doping increased, whereas decreased when the Ce/Ti atomic ratio was greater than 0.5. The optimum atomic ratio of B/Ti and Ce/Ti was 1.6 and 0.5, respectively.
Decoloration and mineralization of yeast wastewater were investigated by using Ce-Fe/Al2O3 as a heterogeneous photo-Fenton catalyst in fluidized bed reactor in order to solve the problem of yeast wastewater discharge. The experimental results were assessed in terms of total organic carbon（TOC） reduction. The operational and reaction conditions affecting the efficiencies of TOC removal such as initial pH value, H2O2 concentration, catalyst loading and UV power were studied. The results show that TOC is reduced from 347.6 mg/L to 10.8 mg/L, color is changed from 500 units to 0 under the conditions as follows： initial pH value 6. 0, H2O2 concentration of 1. 000 g/L, catalyst loading of 5 g/L, reaction duration of 120 rain and reaction temperature of 30 ℃. The irradiated Ce-Fe/Al2O3 catalyst was complexed with 1,10-phenanthroline and then it was subjected to Fourier transform infrared spectroscopy and diffuse reflectance spectroscopy to confirm the formation of Fe（Ⅱ） in the solid state. Heterogeneous photo-Fenton reaction proves to be effective for the treatment of yeast wastewater.