A new kind of reactive toughening accelerator for epoxy resin, amine-teminated hyperbranched polymer (H2O-NMe2) was synthesized and characterized by FT-IR spectroscopy. Dynamic mechanical analysis (DMA) was used to study the glass transition temperature (Tg), loss factor (tanδ) and activation energy (Ea) by using multiplexing frequency. The results show that the Ea at glassy relaxation process of modified system is about 70-80 kJ/mol higher than that of unmodified system, and the high modulus and good thermal properties are still maintained.