The nanometer-size carbides formed in ferrite matrix of Nb-Ti microalloyed steel at different finishing cooling temperatures and holding time have been investigated. The characteristics of nanometer-size carbides in ferrite were observed by transmission electron microscopy, and mechanical properties of ferrite were detected by a nano-hardness tester. The results showed that interphase precipitation and diffusion precipitation were observed at different finishing cooling temperatures, and the interphase precipitation was planar and curved. Sheet spacing of inter-phase precipitation increased with the increase of finishing cooling temperature and changed a little when holding for 50--1000 s. Interphase precipitation shows higher nano-hardness at 640℃ compared with diffusion precipitation at 600℃, and the contribution of interphase precipitation to the mechanical properties of ferrite was larger than that of diffusion precipitation.
Hai-long YIYang XUMing-xue SUNZhen-yu LIUGuo-dong WANG