Ho3＋ doped glasses with various compositions xGeO2-（80-x）TeO2-9.5ZnF2-1ONaF-O.5Ho203 （x=, 10, 20, 30, 40, 50, 60, 70 and 80） were prepared by a melt-quenching technique. The composition-dependent optical transition properties of Ho3＋ were investigated in the framework of Judd-Ofelt theory. The emission cross sections for5I7→5I8 transition of 1-Io3＋ in these glasses were calculated according to McCumber theory, and their compositional dependence was discussed. A simple method was proposed in calculating the emission cross sections of 5I7→5I8 transition, and the calculation results were compared with those derived from McCumber theory. Finally, the optical gain coefficient spectra for 5I7→5I8 transition were also analyzed.
Metal oxide （TiO2 or Co304） doped activated carbon nanofibers （ACNFs） were prepared by electrospinning. These nanofibers were characterized by X-ray diffraction （XRD）, scanning electron microscopy （SEM）, and Brunner- Emmett-Teller method （BET）. The results show that the average diameters of ACNFs were within the range of 200-500 nm, and the lengths were several tens of micrometers. The specific surface areas were 1146.7 m2/g for TiO2-doped ACNFs and 1238.5 m2/g for Co304-doped ACNFs, respectively. The electrospun nanofibers were used for adsorption of low concentration sulfur dioxide （SO2）. The results showed that the adsorption rates of these ACNFs increased with an increase in SO2concentration. When the SO2 concentration was 1.0 μg/mL, the adsorption rates of TiO2-doped ACNFs and Co3Oa-doped ACNFs were 66.2% and 67.1%, respectively. The adsorption rate also increased as the adsorption time increased. When the adsorption time was 40 min, the adsorption rates were 67.6% and 69.0% for TiO2-doped ACNFs and Co304-doped ACNFs, respectively. The adsorption rate decreased as the adsorption temperature increased below 60℃, while it increased as the adsorption temperature increased to more than 60℃.
Eu3＋-doped binary borate glasses with different metal oxide components RO （R=Ca, Sr, Ba, Zn or Pb） were prepared by meltquenching technique. The fluorescent spectral properties of Eu3＋in these glasses were experimentally studied. The analysis on the phonon sidebands （PSBs） indicated that RO component did not cause obvious change of the electron-phonon coupling constant （EPC）. By inspecting the optical absorption edges it was found that RO could greatly affect the band gap energy, and the glass with PbO component revealed the smallest band gap energy, the glasses with ZnO, BaO and SrO showed similar band gap energy. The optical transition intensity parameters of Eu3＋in all studied glasses were calculated, it was found that for each sample its value of2 was larger than that of 4 and 6, and the sample with PbO component exhibited the smallest2, but the λ values for ZBE, CBE, BBE and SBE were very similar. These results might be helpful for the design of borate glasses.