We adopted double-side fabrication process to prepare intrinsic Josephson junctions (IJJs) based on Bi2Sr2CaCu2O8+x (BSCCO) single crystals. Using crystal cleavage and double-side argon ion milling, we have successfully fabricated very uniform IJJs with the thickness of single crystal slice less than 200 nm. Using quasi-optical system, the response of the IJJs to millimeter wave radiation was studied. With applied magnetic field perpendicular to a-b plane, we have observed Shapiro steps under millimeter wave radiation, and the Josephson oscillation of each junction was phase-locking.
WU JingBo YI DongChao GU ZhengHao KANG Lin XU WeiWei CHEN Jian WU PeiHeng
We adopted a new method, acid etching process, to fabricate the intrinsic Josephson junctions based on the Bi2Sr2CaCu2O8+x single crystals. By soaking the crystals into the dilute hydrochloric acid, we fabricated a junction stack successfully, and meantime made the surrounding area insulated. A certain concentration of hydrochloric acid was used to maintain the roughness of the modified layer. The cur-rent-voltage characteristic was achieved through the four terminal measurement. We could control the junctions' number by changing the concentration and the soaking time. We also found that the thick-ness of the stack was equal to the average height of the insulation layer. Such a simple, convenient and controllable fabrication method with a high yield might widen the applications of the intrinsic Joseph-son junctions.
ZHANG Jie CHEN Jian WU JingBo KANG Lin XU WeiWei WU PeiHeng