The effect of temperature on the characteristic of Fourier Transform Infrared(FTIR),the dependence of the average molecular weight and the polydispersity on the annealing temperature and the relationship between linear expansion coefficients and temperature of poly(propylene carbonate) end-capped with maleic anhydride(MA-PPC) were investigated.The vibration peak of hydroxyl group at 1714?cm -1 in the FTIR spectra,which belongs to the carboxyl end-group in MA-PPC,decreases with increasing the temperature of the sample and it disappeared totally when the sample was heated over 70℃.The average molecular weight of MA-PPC almost doubled when the sample was annealed at 110～150℃ for 30 min,however the polydispersity was maintained roughly.A new relaxation transition at about 80℃ was detected on the curve of the linear expansion coefficient versus temperature that is the characteristic of macromolecular coupling or crosslinking reaction.These results confirmed that the macromolecular coupling reaction was carried out between the end carboxyl groups of MA-PPC when the sample was heated over 70℃.
研究了LLDPE g GMA (甲基丙烯酸缩水甘油酯 )对PA66/PE相容性的影响。结果表明LLDPE g GMA是PA66/PE合金良好的反应型增容剂 ,对于PA66/PE合金 ,LLDPE g GMA的加入使合金的拉伸强度、弯曲强度、Izod缺口冲击强度有明显提高。但刚性和耐热性略有降低 ,并且DMA谱图证实了LLDPE g GMA对PA66/PE的反应增容作用 。