Analysis for twinning and slip in face-centered cubic crystals under axisymmetric co-deformation
2006年
The maximum work principle of Bishop-Hill was developed to analyze the axisymmetric co-deformation in face-centered cubic crystals (f.c.c.) for twinning on {111} 112 and slip on {111} 110 systems. The influence of ξ , the ratio of critical re- solved shear stress for twinning to slip, on the yield stress states and corresponding active slip or/and twinning systems for orientations in the standard stereographic triangle of cubic crystal was investigated systematically. The Taylor factors and the anisotropy of yield strength for three important orientations [100], [110] and [111] in orientation space were analyzed. It is found that the yield strength asymmetry for the case of axisymmetric de- formation of tension and compression can be explained based on the microscopic theory of crystal plasticity. The concept of orientation factor for twinning ability was proposed and the deformation mechanism map in the orientation space was established for the case of axisymmetric deformation. The deformation texture formation and development of f.c.c. crystals with low stacking fault energy for axisymmetric tension can be explained qualita- tively on the basis of analyzed results.
CHEN Zhiyong1,2, CAI Hongnian1, ZHANG Xinming2, WANG Fuchi1 & TAN Chengwen1,3 1. School of Material Science and Engineering, Beijing Institute of Technology, Beijing 100081, China
关键词:TWINNING
面心立方晶体孪生和滑移轴对称共生塑性变形分析
2006年
将Bishop-Hill最大功原理拓展于面心立方晶体{111}<112>孪生和{111}<110>滑移两种机制同时起作用的轴对称共生塑性变形过程之中.系统研究了孪生对滑移不同临界剪切应力之比ξ对立方晶体标准投影三角形区各晶体取向的屈服应力状态以及相应活化滑移或/和孪生系的影响,同时分析了取向空间里[100],[110]和[111]三个重要取向的Taylor因子及屈服强度各向异性的变化规律,从微观晶体塑性理论本质上揭示了轴对称变形情况下拉伸和压缩屈服强度的不对称性;引入了孪生能力取向因子概念,建立了轴对称塑性变形取向空间塑性变形机构图.在此基础上,定性地解释了低层错能面心立方晶体在轴对称拉伸情况下形变织构的形成演变规律.
陈志永才鸿年张新明王富耻谭成文
关键词:孪生滑移