Ni-W-B composites containing CeO2 nano-particles on the surface of 45 steel were prepared by pulse electrodeposition,and the in-fluence of pulse frequency,pulse duty circle and heat treatment temperature on the structures and properties were investigated.The results in-dicated that the pulse co-deposition of Ni,W,B and CeO2 nano-particles led to Ni-W-B/CeO2 composites possessing higher microhardness and better wear resistance when heat-treated at 400 oC for 1 h.The microhardness of 636 HV and the deposition rate of 0.0281 mm/h of the as-deposited alloy were the highest at pulse frequency of 1000 Hz,pulse duty circle of 10% and pulse average current density of 10 A/dm2.The composites were mainly in the amorphous state and were partially crystallized as-deposited,and the crystallization trend was strength-ened when heat-treated at 400 oC.Decreasing pulse duty cycle from 75% to 10% was favorable to the refinement in grain structures and im-provement of microstructures.The crystal sizes of the composites were smaller by means of pulse electrodeposition.
Ni-W-P composite coatings reinforced by Ce O2 and Si O2 nano-particles on the surface of common carbon steels, were prepared by double pulse electrodeposition. The crystallization course was characterized by phase structures, crystallinity, grain sizes and microstructures. The results indicate that as-deposited composite coating is amorphous. Whereas it turns into the crystalline structure with 98.25% crystallinity, and Ni3 P, Ni2 P and Ni5P2 alloy phases precipitate from structures at 400 °C. Thereafter, Ni2 P and Ni5P2 metastable alloy phases turn into Ni3 P stable alloy phase at 500 °C. The crystallization course of the composite coating has finished when being heat-treated at 700 °C. The average sizes of Ni grains increase with the rise of heat treatment temperature from400 °C to 700 °C. Ce O2 and Si O2 nano-particles deposited into Ni-W-P alloys can delay the crystallization course and habit the growth of alloy phases.
Ni-W-P matrix composites containing CeO2 and SiO2 nano-particles were prepared on common carbon steel surface by means of pulse electrodeposition,and the high-temperature oxidation behavior was investigated.The results show that when the oxidation time is controlled in 1 h,oxidation kinetics curve between oxidation mass gain rate and oxidation temperature of CeO2-SiO2/Ni-W-P composites accords with the index increasing law.When the oxidation temperature is controlled at 300℃,the kinetics curve between oxidation mass gain rate and oxidation time accords with the linear increasing law.The composites as-deposited are in the amorphous state and turn into the crystal state at 400℃.The microstructures of oxidation film on the composites will change from the compact state to the loose state with increasing oxidation temperature to 800℃.They are still continuous and compact,and there are no crackle,strip and falling-out.CeO2 and SiO2 nano-particles co-deposited into Ni-W-P alloy can improve the high-temperature oxidation resistance.
Ni-W-P matrix composite coatings reinforced by CeO2 and SiO2 nano-particles were prepared on common carbon steel surface by double pulse electrodeposition and the deposition mechanism was discussed.The results showed that the composite coatings with amorphous structure were obtained as-deposited.The initial growth behavior had alternatives and the nucleation was inhomogeneous because of obvious composition fluctuation.With the pulse deposition time increasing,some pearlite microstructures of the substrate were covered by some deposits and the composition fluctuation disappeared.Forward pulse currents promoted to form a great number of atomic beams composed of Ni,W and P atoms or CeO2 and SiO2 nano-particles as the core,which inhabited the growth of atomic beams.Reverse pulse currents eliminated concentration polarization and dissolved some surface boss of atomic beams.The solution of W and P atoms within Ni grains and embedding of CeO2 and SiO2 nano-particles within Ni-W-P matrix metal made atomic arrangement disordered.Finally,the atomic beams grew to amorphous small particles.
Ni-W-P base composites containing CeO2 and SiO2 nano-particles were prepared on common carbon steel surface by pulse co-deposition of Ni,W,P,CeO2 and SiO2 nano-particles.The influence of SiO2 concentrations in bath on microstructures and properties of Ni-W-P/CeO2-SiO2 composites was studied,and the characteristics were assessed by chemical compositions,element distribution,surface morphologies,deposition rate and microhardness.The results indicate that when SiO2 concentration in bath is controlled at 20 g/L,the composites possess the fastest deposition rate,the highest microhardness,compact microstructures,smaller crystallite sizes and uniform distribution of W,P,Ce and Si within Ni-W-P matrix metal.Increasing SiO2 concentration in bath from 10 to 20 g/L leads to the refinement in grain size and the inhomogeneity of microstructures.While when SiO2 concentration is increased to 30 g/L,the crystallite sizes increase again and some bosses with nodulation shape appear on the surface of composites.