Compared with using semi-automatic gas shielded arc welding, using automatic TANDEM twin wire welding and twin wire gas metal arc welding （GMAW） to weld Q690 steel, a low-alloy high-strength structural steel used in the hydraulic support in the fully-mechanized mining face, the welding speed, deposition rate, production environment and welding quality can be obviously improved. Compared with GMAW twin wire welding, a refined micro- structure in the weld and heat-affected zone （HAZ）, narrow HAZ and improved joint strength were achieved with TANDEM on Q690. Also, due to the push-pull pulsed way in TANDEM welding, the droplet transfer, distribution on heat flow and interaction between two arcs were completely different from those in GMAW twin wire system. The heat input of TANDEM is only about 76.6% of GMAW, and correspondingly, the welding speed and welding seam can be obviously improved. The complete oscillation caused by TANDEM pulsed current occurred in the welding pool, which refined the grains in the microstructure. The results show that TANDEM twin wire welding is very suitable in the welding of Q690 used in the hydraulic support.
FANG Chen-fuMENG Xiao-huiHU Qing-xianWANG Feng-jiangREN HeWANG Hai-songGUO YuMAO Ming
Cable welding wire（CWW）CO2gas shielded welding is an innovative process arc welding with high efficiency,high quality and low consumption,in which cable wire is used as consumable electrode.CWW CO2gas shielded welding and submerged arc welding（SAW）are used for contrast studies on processing property of high strength steel A36used in ship structure.The results show that the shapes of weld seam,using CWW CO2gas shielded welding and SAW,are good and no weld defect such as air hole,flaw,slag inclusion,incomplete fusion,lack of penetration and so on are found in the weld seam.Because the rotating of arc during CWW CO2gas shielded welding process has a strong stirring effect on molten pool,the grain in the heat affected zone（HAZ）of the joints,using CWW CO2 gas shielded welding,is small.Tensile failure positions of joints by CWW CO2gas shielded welding and SAW are all in the base metal,but tensile strength of CWW CO2gas shielded welding joint is higher than that of SAW joint by an average of 2.3%.The average impact energy of HAZ,using CWW CO2gas shielded welding and SAW,is almost equal,but the average impact energy of the weld seam using CWW CO2gas shielded welding is increased by 6%,and the average impact energy of the fusion line is increased by 7%.The 180°bending tests for the joints of CWW CO2 gas shielded welding and SAW are all qualified,and the joints hardness is all less than HV 355,but hardness of CWW CO2gas shielded welding wire welding joint near the fusion line is obviously lower.It can be concluded that the properties of CWW CO2gas shielded welding are better than those of the SAW joint,and CWW CO2gas shielded welding is suitable for welding high strength steel A36used in ship structure.