An innovative process of blast furnace （BF） operation involving charging with low-titanium vanadium-titanium magnetite carbon composite hot briquette （LVTM-CCB） was proposed for utilizing LVTM and conserving energy, In this study, the effect of LVTM-CCB charging ratio on the softening, melting, and dripping behaviors of the mixed burden was explored systemically, and the migration of valu- able elements V and Cr was extensively investigated. The results show that with increasing LVTM-CCB charging ratio, the softening inter- val T40 - T4 increases from 146.1℃ to 266.1℃, and the melting interval To - Ts first decreases from 137.2℃ to 129.5℃ and then increases from 129.5℃ to 133.2℃. Moreover, the cohesive zone becomes narrower and then wider, and its location shifts slightly downward. In addi- tion, the recovery ratios of V and Cr in dripped iron first increase and then decrease, reaching maximum values of 14.552% and 28.163%, respectively, when the charging ratio is 25%. A proper LVTM-CCB charging ratio would improve the softening--melting behavior of the mixed burden; however, Ti（C,N） would be generated rapidly in slag when the charging ratio exceeds 25%, which is not favorable for BF op- eration. When considering the comprehensive softening-melting behavior of the mixed burden and the recovery ratios of V and Cr, the rec- ommended LVTM-CCB charging ratio is 20%.
The effect of sinter with different MgO contents on the softening-melting behavior of mixed burden made from chro- mium-bearing vanadium-titanium magnetite was investigated. The results show that with increasing MgO content in the sinter, the softening interval and melting interval increased and the location of the cohesive zone shifted downward slightly and became moderately thicker. The softening-melting characteristic value was less pronounced when the MgO content in the sinter was 2.98wt%-3.40wt%. Increasing MgO content in the sinter reduced the content and recovery of V and Cr in the dripped iron. In addition, greater MgO contents in the sinter resulted in the generation of greater amounts of high-melting-point components, which adversely affected the permeability of the mixed burden. When the softening-melting behavior of the mixed burden and the recovery of valuable elements were taken into account, proper MgO con- tents in the sinter and slag ranged from 2.98wt% to 3.40wt% and from 11.46wt% to 12.72wt%, respectively, for the smelting of burden made from chromium-bearing vanadium-titanium magnetite in a blast furnace.