Based on monomer 2,6,12-triaminotriptycene,hyperbranched polyimides with high molecular weight modified with different terminal functional groups were obtained by polymerization of A_2+B_3 system.The prepared hyperbranched polyimides had good solubility in CHCl_3,DMF and THF,and performed no detective T_gs in the range of 50-330℃and high T_ds(5%) above 455℃.
Based on several unsymmetrical,twist,noncoplanar phthalazinone-containing monomers 2a-2e and an active bis(4-fluorophenyl)phenyl phosphine oxide(BFPPO) monomer,a series of novel poly(phthalazinone ether phosphine oxide)s (PPEPO) was synthesized by anhydrous K_2CO_3 mediated N—C coupling reaction in DMAc.The polymers exhibited good thermal properties with T_gs ranging from 267℃to 306℃and 5%weight loss temperatures in nitrogen higher than 430℃, together with high char yield upon prolonged heating at 800℃(35%—56%).Moreover,the polymers were readily soluble in common organic solvents,such as N-methyl-2-pyrrolidone,chloroform and m-cresol.These polymers had inherent viscosities in the range of 0.45-0.72 dL/g and could be cast into flexible and colorless films by spin coating or casting approach.