The corrosion behavior of C110 bushing at high temperature and high pressure with a high H2S / CO2 was studied, and a basis for the materials selection of sour gas well bushing was provided in H2S, CO2 and saline coexisting environment. Under acidic condiction, hydrogen atoms greatly entered into the material and caused the material properties changed. Weight loss method was used to study the corrosion rate of hydrogen charging samples and original untreated samples in simulated oil field environment. PAR2273 electrochemical workstation was used to examine the electrochemical performance of samples untreated, hydrogen charging after reacting in autoclave. The corrosion product film was observed through SEM. The experimental results show that sample with hydrogen charging has a much more obvious partial corrosion and pitting corrosion than the untreated blank sample even the downhole corrosion speed of bushing is increased after being used for a period of time. Polarization curve shows the corrosion tendency is the same between sample with or without hydrogen charging and corrosion tendency is reduced by corrosion product film. A layer of dense product film formed on the surface of samples provides a certain protective effect to the matrix, but cracked holes which will accelerate partial corrosion of the sample were also observed.
With the aid of hydrogen permeating devices, the hydrogen permeation behaviors of X52 pipeline steel in NACE A solution with saturated H2S/CO2 were studied under the conditions of different ambient temperatures and pH values, and the hydrogen permeation behaviors of X52 pipeline steel in weld seam zone were comparatively studied. The experimental results show that the hydrogen permeation coefficient value is directly proportional to the time required for reaching the saturation anode current and inversely proportional to the saturation anode current, and the hydrogen permeation coefficient is influenced by the corrosion scales; the temperature is directly proportional to the saturation anode current, and the hydrogen permeation coefficient is influenced by the temperature and corrosion scales, heat-affected zone and matrix zone in NACE A solution with saturated H2S/CO2 at normal temperature. The hydrogen permeation coefficient in weld seam zone is larger than that in heat-affected zone which is further larger than that in matrix zone.