Aim To investigate the multiple melting behavior of polyamide 6(PA 6) in polyamide 6/linear low density polyethylene blends crystallized from the crystal amorphous state. Methods\ The effects of annealing temperature, annealing time, heating rate, and the step wise annealing were measured by DSC. Results and Conclusion\ There exists a critical heating rate affecting the middle temperature melting peak. When annealed at the temperature close to the melting peak, the main melting peak of PA 6 shifted to a higher temperature. Within a short time, annealing time has much effect on neat PA 6 but little effect on PA 6 in the blends. Addition of PE results in a decreasing in the height of melting peak. These phenomenon show that the melting behavior of PA 6 was affected by PE, compatibilizer, as well as thermal treatment.
Aim To investigate the melting behavior of polyamide 6 in polyamide 6/polyethy lene blends crystallized from amorphous state. Methods DSC was used to test effects of annealing temperature, annealing time, DSC scan rate, and the step wise annealing on the melting peaks of the ice water quenched specimens. Results and Conclusion Varied melting peaks of PA6 component were obtained. The degree of perfection and the crystallization degree of PA6 crystals decreased in the blends, and the crystallization degree of PA6 increased with the increasing of the annealing time. The height of the upper melting peak of reference PA6 is higher than that in blends.