Room-temperature mechanical properties of Cu50Zr40Ti10-xNix（0≤x≤4,mole fraction,%） bulk metallic glasses （BMG） with aspect ratios in the range of 1：1-2.5：1 and loading rates in the range of1×10^-5-1×10^-2s^-1were systematically investigated by room-temperatureuniaxialcompression test.In the condition of an aspect ratio of 1：1, the superplasticity can be clearly observed for Cu50Zr40Ti10BMG when the loading rate is1×10^-4s^-1, while for Cu50Zr40Ti10-xNix（x=1-3, mole fraction, %） BMGs when the loading rate is1×10^-2s^-1. The plastic strain （εp）, yielding strength （σy） and fracture strength （σf） of the studied Cu-based BMGs significantly depend on the aspect ratio and the loading rate. In addition, theσyof the studied Cu-based BMGs with an aspect ratio of 1：1 is close to the σfof those with the other aspect ratios when the loading rate is1×10^-2s^-1. The mechanism for the mechanical response to the loading rate and the aspect ratiowas also discussed.