New strain induced melt activation（new SIMA） method was employed to prepare high-quality semisolid billet of AZ61 magnesium alloy.Optical microscopy and tensile test were used to study the microstructure and mechanical properties of the thixo-extruded component.The results showed that the optimal process parameters for achieving the complete filling status involved the applied pressure of 784 MPa,the pressure holding time of 90 s and the die temperature of 450 ℃.Compared to semisolid isothermal treatment,high mechanical properties such as the tensile strength of 300.5 MPa and elongation of 22% and fine microstructure were obtained in the thixo-extruded parts.With increasing the isothermal temperature and holding time,the tensile strength and elongation were increased firstly and then decreased.When the press pass was increased from 1 to 4,the tensile strength and elongation of the thixo-extruded parts were greatly enhanced and microstructure was refined obviously.