The effect of temperature on the characteristic of Fourier Transform Infrared(FTIR),the dependence of the average molecular weight and the polydispersity on the annealing temperature and the relationship between linear expansion coefficients and temperature of poly(propylene carbonate) end-capped with maleic anhydride(MA-PPC) were investigated.The vibration peak of hydroxyl group at 1714?cm -1 in the FTIR spectra,which belongs to the carboxyl end-group in MA-PPC,decreases with increasing the temperature of the sample and it disappeared totally when the sample was heated over 70℃.The average molecular weight of MA-PPC almost doubled when the sample was annealed at 110～150℃ for 30 min,however the polydispersity was maintained roughly.A new relaxation transition at about 80℃ was detected on the curve of the linear expansion coefficient versus temperature that is the characteristic of macromolecular coupling or crosslinking reaction.These results confirmed that the macromolecular coupling reaction was carried out between the end carboxyl groups of MA-PPC when the sample was heated over 70℃.
以过氧化二异丙苯 (DCP)为引发剂 ,甲基丙烯酸缩水甘油酯 (GMA)为活性单体 ,高抗冲苯乙烯(HIPS)通过熔融接枝制得了功能化的高抗冲聚苯乙烯接枝物 (HIPS g GMA)。用红外光谱和电子能谱对其结构进行了表征。HIPS g GMA的红外谱图 ,证明GMA已经接枝到HIPS上。电子能谱分析也提供了相似的结论。研究了单体浓度和DCP用量对产物接枝率的影响 ,并用化学滴定方法测定了接枝物的接枝率。用DSC、SEM、WAXD、DMA等研究了PBT/HIPS和PBT/HIPS g GMA的结晶、形态结构、动态力学性能及力学性能随组成的变化。SEM及DMA分析表明增容后体系的相容性得到改善 ,力学性能有较大提高。